Flame retardant materials from 3D printing

• Density [g/cm3] 1.2
• E-modul [Gpa] 3
• Flexural strength [MPa] 71
• Flexural modulus [Gpa] 3.6
• Heat deflection temp @0.45MPa [°C] 145

Plastic with good chemical resistance, flame retardant

• Especially suitable for lightweight construction

• Density [g/cm3] 1.27
• Tensile strength [MPa] 70
• E-modul [Gpa] 2.51
• Flexural strength [MPa] 100
• Flexural modulus [Gpa] 2.4
• Impact resistance (Izod notched) [J/m] 88
• Heat deflection temp @1.81MPa [°C] 173
• Elongation at break [%] 5.7

PETG equipped with flame retardant (halogen-free), meets UL94 HB and UL94 V0 test specifications for flame retardant materials.

• Color: Black matt
• modulus of elasticity (UNE-EN ISO 527-2): 2980 MPa
• Tensile strength (UNE-EN ISO 527-2): 51 MPa
• Tensile elongation (UNE-EN ISO 527-2): 129%.
• Heat deflection temperature (UNE-EN ISO 306): 80 °C
• RoHS and REACH compliant
• Flame retardant (UL94 V0 classification)